中國有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 32 No. 7 July 2022 |
（1. State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, China;
2. AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China）
Abstract:The hot deformation behavior and microstructure evolution of 6082 aluminum alloy fabricated through squeeze casting (SC) under different pressures were studied. The alloy was subjected to hot compression tests and 3D hot processing maps were established. The microstructure evolution was studied by optical microscope (OM), scanning electron microscope (SEM), and electron backscattered diffraction (EBSD). It is found that more dynamic recrystallization (DRX) grains are generated during the deformation of the specimen fabricated under higher SC pressure. At high temperature the effect of SC pressure on microstructure evolution weakens due to the dissolution of second phase particles. In addition, uneven second phase particles in specimens fabricated under higher SC pressure compressed with low temperature and middle strain rate would result in flow localization instability. Finally, the optimum deformation conditions for the 6082 aluminum alloy fabricated by SC were obtained at the temperatures of 430-500 °C and the strain rates of 0.01-1 s-1.
Key words: 6082 aluminum alloy; squeeze casting; deformation behavior; processing map; dynamic recrystallization