Abstract:Ti-based scaffolds reinforced with zirconia and hydroxyapatite were produced successfully by a hybrid method with an eco-friendliness and low cost to obtain low elastic modulus (E) with sufficient physical, electrochemical and biological properties. The effect of simultaneous modification of the volume fraction of hydroxyapatite (HA) and zirconia (ZrO₂) on scaffolds was investigated in terms of mechanical, corrosive, and antibacterial properties. Scanning electron microscopy with attached electron dispersive spectroscopy and X-ray diffraction were used for the characterization of scaffolds. Compression and electrochemical tests were performed to determine mechanical properties with detailed fracture mechanism and in-vitro corrosion susceptibility to simulated body fluid at 37 °C, respectively. Antibacterial tests were carried out by comparing the inhibition areas of E.coli and S.aureus bacteria. It was observed that the mechanical strength of the scaffolds decreased with increasing HA:ZrO₂volume fraction ratio. The lowest E was achieved (6.61 GPa) in 6:4 HA:ZrO₂ composite scaffolds. Corrosion current density (J_corr) values were calculated to be21, 337, and 504 μA/cm² for unreinforced Ti, 3:2 and 6:4 HA:ZrO₂ reinforced scaffolds, respectively. The inhibition capacity of the 6:4 reinforced composite scaffold was found to be more effective against S.aureus bacteria than other scaffolds.

Key words: titanium biocomposite; hydroxyapatite; zirconia; scaffold; mechanical properties; in-vitro corrosion