Abstract:The effects of Fe content on the microstructure, phase constituents and microhardness of the as-cast, 800 °C- or 1000 °C-annealed Al₇Cr₂₀Fe_xNi_73-x (x=13-66) alloys were investigated. Not all these alloys are composed of the single FCC phase. The BCC and B2 phases are found. It is confirmed that the BCC phase in the Al₇Cr₂₀Fe₆₆Ni₇ alloy is transformed from the FCC phase at about 900 °C during cooling. While in the 800 °C-annealed Al₇Cr₂₀Fe₆₀Ni₁₃ alloy, the FCC phase is stable and the hardness decreases. After annealing at 1000 °C, for the precipitation of the B2 particles, the Al content in the FCC phase decreases, which results in decreasing of the alloy hardness. Moreover, after annealing at 800 °C, a small amount of Al-rich B2 particles precipitate at the phase boundary and some nanocrystal BCC phase precipitates in the FCC matrix, which increases the hardness of the Al₇Cr₂₀Fe_xNi_73-x (x=41-49) alloys. These results will help to the composition design and processing design of the Al-Cr-Fe-Ni based high-entropy alloys.

Key words: high-entropy alloy; Al-Cr-Fe-Ni; phase constituent; microhardness; heat treatment