中國(guó)有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 31 No. 1 January 2021 |
（1. Institute of Solidification Science and Technology, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, China;
2. Shanghai Key Laboratory of Advanced High-temperature Materials and Precision Forming, Shanghai Jiao Tong University, Shanghai 200240, China;
3. School of Aerospace Engineering, Beijing Institute of Technology, Beijing 100081, China;
4. State Key Laboratory of Tribology, Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China;）
Abstract:Ti-6Al-4V alloy was fabricated via selective laser melting (SLM) to improve its corrosion resistance for implant. The microstructure and electrochemical corrosion behavior were investigated using scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), transmission electron microscopy (TEM), electrochemical test and contact angle test. It can be found that the as-selective laser melted (as-SLMed) Ti-6Al-4V alloys show β columnar microstructure in building direction and nearly circular checkerboard microstructure in scanning direction, while the wrought and wrought+HT samples exhibit equiaxed microstructure. The as-SLMed Ti-6Al-4V alloy exhibits better corrosion resistance than the wrought and wrought+HT samples due to hydrophobicity, high grain boundary density and uniform distribution of alloying elements in simulated artificial saliva at 37 °C.
Key words: Ti-6Al-4V alloy; selective laser melting; microstructure; electrochemical corrosion behavior