Abstract:Combustion synthesis involving metallothermic reduction of Fe₂O₃ and TiO₂ was conducted in the mode of self-propagating high-temperature synthesis (SHS) to fabricate FeAl-based composites with dual ceramic phases, TiB₂/Al₂O₃ and TiC/Al₂O₃. The reactant mixture included thermite reagents of 0.6Fe₂O₃+0.6TiO₂+2Al, and elemental Fe, Al, boron, and carbon powders. The formation of xFeAl-0.6TiB₂-Al₂O₃ composites with x=2.0-3.6 and yFeAl-0.6TiC-Al₂O₃ composites with y=1.8-2.75 was studied. The increase of FeAl causes a decrease in the reaction exothermicity, thus resulting in the existence of flammability limits of x=3.6 and y=2.75 for the SHS reactions. Based on combustion wave kinetics, the activation energies of E_a=97.1 and 101.1 kJ/mol are deduced for the metallothermic SHS reactions. XRD analyses confirm in situ formation of FeAl/TiB₂/Al₂O₃ and FeAl/TiC/Al₂O₃ composites. SEM micrographs exhibit that FeAl is formed with a dense polycrystalline structure, and the ceramic phases, TiB₂, TiC, and Al₂O₃, are micro-sized discrete particles. The synthesized FeAl-TiB₂-Al₂O₃ and FeAl-TiC-Al₂O₃ composites exhibit the hardness ranging from 12.8 to 16.6 GPa and fracture toughness from 7.93 to 9.84 MPa·m^1/2.

Key words: FeAl-based composites; self-propagating high-temperature synthesis; metallothermic reduction; activation energy