Abstract:The effect of hot compression on the grain boundary segregation and precipitation behavior of M₆C carbide in the Ni-20Cr-18W-1Mo superalloy was investigated by thermomechanical simulator, scanning electronic microscope (SEM) and X-ray diffraction (XRD). Results indicate that the amount of M₆C carbides obviously increases in the experimental alloy after hot compression. Composition analyses reveal that secondary M₆C carbides at grain boundaries are highly enriched in tungsten. Meanwhile, the secondary carbide size of compressive samples is 3-5 μm in 10% deformation degree, while the carbide size of undeformed specimens is less than 1 μm under aging treatment at 900 and 1000 °C. According to the thermodynamic calculation results, the Gibbs free energy of γ-matrix and carbides decreases with increase of the compression temperature, and the W-rich M₆C carbide is more stable than Cr-rich M₂₃C₆. Compared with the experimental results, it is found that compressive stress accelerates the W segregation rate in grain boundary region, and further rises the rapid growth of W-rich M₆C as compared with the undeformed one.

Key words: Ni-20Cr-18W-1Mo superalloy; hot compression; grain boundary segregation; carbide precipitation