Abstract:Mullite–zirconia composites containing 20% zirconia (mass fraction) were prepared by reaction sintering route utilizing Indian coastal zircon flour and sillimanite beach sand. 4%-12% of CaO (mole fraction) with respect to zirconia was used as additive. The effect of additive on densification, microstructure as well as various mechanical and thermo-mechanical properties was studied. Incorporation of CaO reduced the densification temperature of the composites to 1550 °C compared to 1600 °C (for CaO free samples). CaO formed small amount of liquid phase (calcium aluminosilicate), which facilitated sintering. Average grain size of the composites decreased up to 4% CaO addition, afterwards grain size increased with further addition of CaO. Samples with 4% CaO exhibited ~225 MPa of flexural strength, ~6 MPa·m^1/2 of fracture toughness and significant improvement in thermal shock resistance. CaO stabilized the tetragonal zirconia phase and thus improved the mechanical properties.

Key words: reaction sintering; mullite-zirconia composites; flexural strength; refractory