Abstract:The effect of iron addition on the microstructure, mechanical and magnetic properties of Al-matrix composite was studied. Mechanical mixing was used for the preparation of 0, 5%, 10% and 15% Fe-Al composites (mass fraction). Mixtures of Al-Fe were compacted and sintered in a vacuum furnace at 600 °C for 1 h. X-ray diffraction (XRD) of the samples containing 5% and 10% Fe indicates the presence of Al and Fe peaks, while sample containing 15% Fe reveals Al and Al₁₃Fe₄ peaks. The results show that both densification and thermal conductivity of the composites decrease by increasing the iron content. The presence of iron in the composite improves the compressive strength and the hardness. The strengthening mechanism is associated with the grain refinement of the matrix and uniform distribution of the Fe particles, as well as the formation of Al₁₃Fe₄ intermetallic. The measured magnetization values are equal to 0.3816×10^{-3 A？m2}/g for 5% Fe sample and increases up to 0.6597×10^{-3 A？m2}/g for 10% Fe sample, then decreases to 0.0702×10^{-3 A？m2}/g for 15% Fe sample. This can be explained by the formation of the diamagnetic Al₁₃Fe₄ intermetallic compound in the higher Fe content sample detected by XRD analysis.

Key words: Al-Fe composite; powder metallurgy; microstructure; mechanical properties; magnetic properties