(湖南大學(xué)化學(xué)化工系，長沙410082)
摘 要: 通過“熱攪拌聚合”方法從石油瀝青和煤瀝青中制備瀝青中間相，再經(jīng)磨粉、活化調(diào)整、模壓和燒結(jié)工藝處理，制得具有自燒結(jié)功能的新型無粘結(jié)劑炭素材料，其抗彎強度高達50MPa。中間相粉末的R值對這種材料的最終性能有很大影響，適宜的R值在0.2~0.3之間。
關(guān)鍵字: 瀝青中間相 自燒結(jié)性 高強度炭素材料
OF HIGH STRENGTH CARBON MATERIAL
（Department of Chemical Engineering, Hunan University, Changsha 410082）
Abstract:By means of“heating stirring polymerization”, pitch mesophase was prepared from petroleum pitch and coal tar pitch. Through the following processing, such as grinding, activating adjustment, moulding and sintering, a new type of binderless carbon material with self-sintering function was made from the pitch mesophase. The flexural strength of the material is higher than 50MPa. TheRvalue of the mesophase powder has significant influence on the final properties of the material, and the suitableRvalue is 0.2~0.3.
Key words: pitch mesophase self sintering high strength carbon material