EuCl3-CaCl2二元系相圖
張俊卿 吳志華 李玉生 王明生
(包頭鋼鐵學(xué)院冶金系， 包頭 014010)
摘 要: 用差熱分析法研究了EuCl3-CaCl2二元體系相圖，發(fā)現(xiàn)該體系有一個(gè)異份熔化化合物EuCl3·3CaCl2。體系轉(zhuǎn)熔點(diǎn)為570 ℃，EuCl3摩爾分?jǐn)?shù)45.4％；低共熔點(diǎn)為522 ℃， EuCl3摩爾分?jǐn)?shù)66.8%。
關(guān)鍵字: EuCl3-CaCl2 二元體系 相圖
PHASE DIAGRAM OF BINARY SYSTEM EuCl3-CaCl2
Zhang Junqing, Wu Zhihua, Li Yusheng, Wang Mingsheng
（Dept.Metallurgy, Baotou University of Iron and Steel Technology， Baotou 014010）
Abstract:The phase diagram of binary system EuCl3-CaCl2 was determined by DTA. In the EuCl3-CaCl2 system, an incongruent compound EuCl3·3CaCl2 , a peritectic point at 570 ℃, containing EuCl3 45.4%(in mole per cent) and an eutectic point at 522 ℃, containing EuCl3 66.8%(in mole per cent) were obtained.