(中南工業(yè)大學非平衡材料科學與工程研究所，長沙 410083)
摘 要: 研究了6061Al/SiCp顆粒增強復合材料的噴射沉積+熱擠壓工藝及材料的組織特征與力學性能。噴射沉積工藝可以獲得增強顆粒均勻分布，無界面反應的大尺寸復合材料錠坯，實驗錠坯尺寸達d200 mm×250 mm，熱擠壓工藝進一步使錠坯致密，增強顆粒分布改善。擠壓材料組織細小，過飽和度大，析出相細小、分布彌散，峰時效時間 約為傳統(tǒng)制度的一半, 且力學性能極大地改善，可達σb=439 MPa,σ0.2=409 MPa，δ=10.4%。
關鍵字: 噴射沉積 復合材料 鋁合金 碳化硅
（Institute of Non-equilibrium Materials Science and Technology,
Central South University of Technology, Changsha 410083, P. R. China）
Abstract:Spray deposition and hot extrusion process for producing 6061Al/SiCp composites and the material's microstructure feature and mechanical properties were studied. As-sprayed large scale composites have uniformly distributed reinforcing particles, and there is no apparent interface reaction. Hot extrusion can densify billets and improve the distribution of particles. As-extruded microstructure is fine and of excess solution, with fine and discattered precipitates. The peak aging time is half that of traditional ones. The mechanical properties improve greatly, and are up to σb=439 MPa, σ0.2=409 MPa, δ=10.4%.
Key words: spray deposition composites mechanical properties
silicon carbide