(武漢工業(yè)大學材料復合新技術國家重點實驗室， 武漢 430070)
摘 要: 采用微波燒結新技術研究了WC-Co細晶硬質(zhì)合金的燒結工藝與性能，并同常規(guī)燒結工藝進行了比較。結果表明：微波燒結WC-Co細晶硬質(zhì)合金在1300℃的燒結溫度下保溫10 min時， 可達到99.8%的相對密度； 燒結溫度降低，燒結時間大幅度縮短，且制品的顯微晶粒尺寸只有常規(guī)燒結的一半；抗彎強度、矯頑磁力、硬度有較大幅度提高。
關鍵字: 微波燒結； 鈷鎢硬質(zhì)合金； 工藝； 性能
（State Key Laboratory of Advanced Technology for Materials Synthesis and Processing,
Wuhan University of Technology, Wuhan 430070, P.R.China）
Abstract:Using the microwave sintering new technology, the technology and property of WC-Co fine grain cemented carbide in microwave sintering was studied and compared with conventional sintering technology. The results show that microwave sintered WC-Co fine grain cemented carbide can reach 99.8% relative density in 1300℃ sintering temperature and 10 min preservation. The microwave sintering not only can reduce sintering temperature and shorten sintering time in large range, but also can decrease micro-grain size of products over less one-half and increase bending strength, coercive force and hardness in large range compared with conventional sintering .
Key words: microwave sintering；WC-Co cemented carbide；technology；properties