(中南工業(yè)大學(xué)材料科學(xué)與工程系，長(zhǎng)沙 410083)
摘 要: 研究了含氮、鈮和稀土的Fe-Cr-Ni耐熱鋼的力學(xué)性能和高溫特性，結(jié)果表明：含0.14%N，0.08%RE，0.15%Nb, 23%～30%Cr和11%～16%Ni的材料經(jīng)1100 ℃水淬，1000 ℃時(shí)效熱處理后具有最好的綜合性能；該材料1 000 ℃時(shí)的抗氧化性能與ZG40Cr25Ni20相當(dāng)，優(yōu)于ZG 35Cr18Ni25Si2等國(guó)內(nèi)外常用的耐熱鋼。
關(guān)鍵字: 耐熱鋼 力學(xué)性能 高溫特性
（Department of Materials Science and Engineering,
Central South University of Technology, Changsha 410083, P. R. China）
Abstract:The mechanical properties and high temperature characteristics of Fe-Cr-Ni heat resistant steels containing nitrogen, niobium and rare-earth were studied. The results show that the comprehensive properties of the material containing 0.14%N, 0. 08%RE, 0.15%Nb, 23～30%Cr, 11～16%Ni after water quenching at 1100 ℃, then aging at 1 000℃ are the best. The oxidation resistance of the above mentioned material at 1000℃ is similar to ZG40Cr25Ni20 and higher than that of traditional heat-resistant steels such as ZG35Cr18Ni25Si2 steel.
Key words: heat-resistant steels; mechanical property; high temperature characteristic