Abstract:The high temperature proton conductor BaZr0.45Ce0.45Gd0.1O3−δ was synthesized by solid-state reaction. The phase composition, microstructures and electrical conducting property of samples sintered at different temperatures were investigated by XRD, SEM and AC impedance spectroscopy. The chemical stability of specimen in boiling water and CO2 atmosphere was tested. The results indicate that the sample sintered at 1 600 ℃ is single phase, with high density and electrical conductivity. Its conductivity at 800 ℃ reaches 0.82×10−2 S/cm. The conducting activity energy is 0.74 eV. BaZr0.45Ce0.45Gd0.1O3−δ shows better chemical stability against carbon dioxide than boiling water.