(1. 上海大學 現(xiàn)代冶金與材料制備重點實驗室，上海 200072；2. 興業(yè)電子銅帶有限公司，慈溪 315336)
摘 要:
關(guān)鍵字: 銅熔體；水平連鑄；電磁攪拌；流動；凝固
（1. School of Materials, Shanghai University, Shanghai 200072, China; 2. Sunshine Electronic Copper-tape Ltd. Co., Cixi 315336, China）
Abstract:A new horizontal electromagnetic stirring method in mold based on the orthogonal interaction between static magnetic field and DC current was put forward to overcome the solidification disadvantages such as micro pore, inclusion and columnar crystals joint in copper thin-slab’s horizontal continuous casting. Commercial production was experimented based on the physical simulation in laboratory. In the simulation, the flow rule of melt metal in mold of horizontal continuous casting with electromagnetic stirring is measured using ultrasonic Doppler velometer, and the result is inter confirmed with the solidification characteristics is tics of zinc cupronickel thin slab in industrial product, some advantageous results are obtained that, when the current is 400 A the inner micro-pores disappear, when the current is 500 A the center equiaxed crystal layers occur and when the current is to 800 A the inner-segregation decreases to zero.
Key words: copper melt; horizontal continuous casting; electromagnetic stirring; flow; solidification