摘 要:
使用不同C與N摩爾比的Ti(C, N)固溶體粉末作為基體材料，采用真空燒結(jié)工藝研制兩種Ti(C, N)基金屬陶瓷刀片試樣，并考察兩種刀片試樣和日本住友T
關(guān)鍵字: Ti(C, N)基金屬陶瓷；刀具；高速切削；磨損
（1. School of Mechatronic Engineering, Hunan University of Science and Technology, Xiangtan 411201, China;
2. School of Mechatronic Engineering, China University of Mining and Technology, Xuzhou 221008, China）
Abstract:Two Ti(C, N)-based cermet inserts samples were fabricated by using Ti(C, N) solid solution matrix with different molar ratios of C to N and vacuum sintering process. The cutting performance of sample A, sample B and T1200A in the dry cutting 20CrMn steel were studied. The morphologies and microstructure of crater and flank wear were observed by using a scanning electron microscope. The wear mechanism of Ti(C, N)-based cermet tools in high speed cutting was discussed. The results show that the Ti(C, N)-based cermet tools are dominated by adhesion, diffusion and oxidation wear in high speed cutting. And decreasing the ratio of C to N in Ti(C, N) solid solution is helpful to improve the resisting wear capability of Ti(C, N)-based cermet tools.
Key words: Ti(C, N)-based cermet; cutting tool; high-speed cutting; wear