Abstract:Nano composite coatings were prepared on MB8 wrought magnesium alloy by electrodeposition with sulfate nickel as main salt. The microstructure of the composite coatings were observed with scanning electron microscopy and transmission electron microscopy, its phase compositions were analyzed with X-ray diffractometry, its microhardness was determined with microhardness meter, its abrasive resistance was tested by rapid abrasive test, and its polarization curve in 3.5% (mass fraction) sodium chloride solution was determined by electrochemical tester. The results show that nano composite coatings with uniform crystalline, dense structure and better corrosion resistance can be obtained on MB8 wrought magnesium alloy and its maximum microhardness reaches HV 682. Moreover, the abrasive resistance of the composite coatings is superior to that of the hard chromium coating, the corrosion potential is increased by 677 mV compared with base Mg alloy.
Key words: MB8 magnesium alloy; electrodeposition; nano composite coating; nano-SiC