(1. 西安理工大學(xué) 材料科學(xué)與工程學(xué)院，西安 710048;
2. 洛陽理工學(xué)院 材料工程系，洛陽 471023;
3. 河南科技大學(xué) 材料科學(xué)與工程學(xué)院，洛陽 471003;
4. 洛陽船舶材料研究所，洛陽471039)
摘 要:
關(guān)鍵字: 熱浸鍍鋁；鋁-鐵合金液；稀土；非晶
layer of steel
ZHANG Zhi-qiang4, GUO Xian-jun2
（1. School of Materials Science and Engineering, Xi’an University of Technology,
Xi ’an 710048, China;
2. Department of Materials Engineering, Luoyang Institute of Science and Technology,
Luoyang 471023, China;
3. School of Materials Science and Engineering, Henan University of Science
and Technology,Luoyang 471003, China;
4. Luoyang Ship Materials Research Institute, Luoyang 471039, China）
Abstract:The microstructure and composition in hot dip aluminized layer of steel were investigated through scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffractometry (XRD) and energy dispersive spectroscopy (EDS). The amorphous phase is found in the outer layer of hot-dip aluminized layer. In order to clear the phenomenon, the Al-Fe alloy liquids used in hot dip aluminizing were quickly solidified and slowly solidified respectively. The results show that under quick solidification both Al-Fe alloy samples with or without La contain amorphous phase. While the Al-Fe alloy liquids are solidified slowly, the amorphous phase is only found in sample with La.
Key words: hot-dip aluminizing; Al-Fe alloy liquid; rare earths; amorphous phase