中國有色金屬學(xué)報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 22 No. 10 October 2012 |
（1. School of Science, Xi’an University of Technology, Xi’an 710048, China;
2. Department of Chemical and Biological Engineering and Engineering Research Institute,
Gyeongsang National University, 900 Gajwa-dong, Jinju 600-701, Korea）
Abstract:Nanosphere-like Li2FeSiO4/C was synthesized via a solution method using sucrose as carbon sources under a mild condition of time-saving and energy-saving, followed by sintering at high temperatures for crystallization. The amount of carbon in the composite is less than 10% (mass fraction), and the X-ray diffraction result confirms that the sample is of pure single phase indexed with the orthorhombic Pmn21 space group. The particle size of the Li2FeSiO4/C synthesized at 700 °C for 9 h is very fine and spherical-like with a size of 200 nm. The electrochemical performance of this material, including reversible capacity, cycle number, and charge-discharge characteristics, were tested. The cell of this sample can deliver a discharge capacity of 166 mA·h/g at C/20 rate in the first three cycles. After 30 cycles, the capacity decreases to 158 mA·h/g, and the capacity retention is up to 95%. The results show that this method can prepare nanosphere-like Li2FeSiO4/C composite with good electrochemical performance.
Key words: lithium-ion batteries; cathode material; Li2FeSiO4/C; solution method