Abstract:Microstructures of as-cast and extruded ZK60-xRE (RE=Dy, Ho and Gd, x=0-5, mass fraction) alloys were investigated. Meanwhile, the impact toughness was tested and then the relationship was discussed. The results show that as-cast microstructure is refined gradually with increasing the RE content. Mg-Zn-RE new phase increases gradually, while MgZn₂ phase decreases gradually to disappear. Second phase tends to distribute along grain boundary in continuous network. Extruded microstructure is refined obviously to reach the micron level. Broken second phase tends to distribute along the extrusion direction in zonal shape. Impact toughness value a_nK increases from 9-17 J/cm² for as-cast state to 26-54 J/cm² for extruded state. With increasing the value of a_nK, fracture macro-morphology changes from a rough plane via multi-plane with step to V-type plane; and from single radiation zone to two zones of fiber and shear lip, respectively. Fracture micro-morphology changes from the brittle fracture to the ductile fracture. Fine grain and few fine dispersed second phase can enhance the impact toughness of magnesium alloys effectively.

Key words: ZK60 magnesium alloys; rare earth; alloying; impact toughness; microstructure; fracture morphology