中國(guó)有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 21 No. 11 November 2011 |
2A50 aluminum alloy prepared by liquid forging
LI Hong-wei3, 4, ZHANG Xin3, 4, XIE Shui-sheng
（1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
2. State Key Laboratory for Fabrication and Processing of Nonferrous Metals,
Beijing General Research Institute for Nonferrous Metals, Beijing 100088, China;
3. Beijing Engineering Research Center for Advanced Manufacturing and Elevation of Special Vehicle Parts,
Beijing 100072, China;
4. Technology Institute, Beijing North Vehicle Group Corporation, Beijing 100072, China）
Abstract:The homogenization on microstructure and mechanical properties of 2A50 aluminum alloy prepared by liquid forging was investigated. Wheel hubs were produced using direct and compound loading. The results show that the microstructure and mechanical properties are inhomogeneous in direct forged samples. The microstructure of the wall is coarser than that of the base, and the mechanical properties are lower and some defects are detected at the wheel corner. Using compound loading, the microstructure and mechanical properties of the wall are improved evidently. With increasing feeding amount, the microstructure and mechanical properties become more homogeneous. The defects disappear when the feeding amount is 4 mm. The forged wheel hubs could obtain fine and homogeneous microstructure with grain size of 20−30 µm, tensile strength of 355 MPa and elongation of 10% when the feeding amount is 10 mm. The microstructure and mechanical properties of liquid forged workpieces could be controlled and homogenized using compound loading.
Key words: homogenization; aluminum alloy; liquid forging; compound loading