Abstract:Directionally solidified (DS) specimens of Nb-Ti-Si based ultrahigh temperature alloy were heat-treated at (1 500 °C, 50 h) and (1 500 °C, 50 h) + (1 100 °C, 50 h), respectively. The results show that the microstructures become uniform, the long and big primary (Nb,X)₅Si₃ (X represents Ti and Hf elements) plates in the DS specimens are broken into small ones, and the eutectic cells lose their lamellar morphology and their interfaces become blurry after heat-treatment. Meanwhile, the (Nb,X)₅Si₃ slices in the eutectic cells of the DS specimens coarsen obviously after heat-treatment. Homogenizing and aging treatments could effectively eliminate elemental microsegregation, and the segregation ratios of all elements in niobium solid solution (Nbss) in different regions tend to 1. After heat-treatment, the microhardness of retained eutectic cells increases evidently, and the maximum value reaches  HV1 404.57 for the specimen directionally solidified with a withdrawing rate of 100 μm/s and then heat-treated at (1 500 °C, 50 h) + (1 100 °C, 50 h), which is 72.8 % higher than that under DS condition.

Key words: Nb-Ti-Si based ultrahigh temperature alloy; homogenizing treatment; aging treatment; microstructural evolution; microhardness