中國有色金屬學報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 20 No. 9 September 2010 |
cast semi-solid 206 alloys
（1. Rio Tinto Alcan, Arvida Research and Development Centre, Jonquière, QC, G7S 4K8, Canada;
2. Rio Tinto Alcan, Laterrière Works, Laterrière, QC, G7N 1A2, Canada;
3. NRC-Aluminium Technology Centre, Chicoutimi, QC, G7H 8C3, Canada;
4. Université du Québec à Chicoutimi, Chicoutimi, QC, G7H 2B1, Canada）
Abstract:The development of a modified 206 alloy whose composition was optimized to minimize hot tearing during semi-solid forming was reported. The effect of varying silicon, copper and iron contents was investigated using a design of experiment (DOE) approach. Semi-solid slurries were prepared using the SEED process and injected into a high pressure die casting press. The hot tearing sensitivity results were reported for different alloy variants. The microstructure evolution during the semi-solid preparation was presented along with actual die cast components. The effects of silicon, copper and iron on mechanical properties in the T7 condition were also analyzed. Beyond the benefit of reducing hot tearing, it is shown that the tensile and fatigue properties remain compatible with the automotive industry requirements.
Key words: semi-solid forming; 206 aluminum alloy; SEED process; hot tearing; mechanical properties