中國(guó)有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 20 No. 7 July 2010 |
mechanical properties of ZA54 alloy
XU Chun-xiang(許春香)1, WANG Xiao-ming(王曉明)2, YAN Jie(嚴(yán) 杰)
（1. College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China;
2. CSR Qishuyan Locomotive and Rolling Stock Technology Research Institute Co. Ltd., Changzhou 213011, China）
Abstract:To improve the strength, toughness and heat-resistance of magnesium alloy, the microstructure and mechanical properties of ZA54 alloy reinforced by icosahedral quasicrystal phase (I-phase) particles were studied. Except α-Mg, φ-phase and τ-phase, MgZnYMn I-phase particles can be obtained in ZA54-based composites by the addition of icosahedral quasicrystal-contained Mg-Zn-Y-Mn master alloy. The introduction of MgZnYMn I-phase into ZA54 alloy has great contribution to the refinement of matrix microstructures and the improvement of mechanical properties. When the addition of Mg-based spherical quasicrystal master alloy is up to 3.5% (mass fraction), the macro-hardness of ZA54-based composites is increased to HB 68. The impact toughness of composites reaches the peak value of 18.3 J/cm2, which is about 29% higher than that of ZA54 mother alloy. The highest tensile properties at ambient and elevated temperatures with master alloy addition of 2.5% (473 K) are also obtained in ZA54-based composites with 3.5% (mass fraction) Mg-Zn-Y-Mn master alloy addition. The ultimate tensile strength of composites at ambient and elevated temperatures are 192.5 MPa and 174 MPa, which are 23.4% and 33.8% higher than that of ZA54 mother alloy, respectively. The improved mechanical properties are mainly attributed to the pinning effect of I-phase on grain boundaries.
Key words: magnesium alloy; spherical quasicrystal particles; ZA54 alloy; composite strengthening; heat-resistance