中國(guó)有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 10 No. 1 February 2000 |
（Department of Metallurgy, Kunming University of Science and Technology, Kunming650093, P.R.China）
Abstract:The components and microstructure of the RE-Ni-W-P-SiC composite coating were analyzed by means of EPXDS, SEM and XRD. The results showed that the composite coating containing 5%~14%RE, 4%~7%SiC, 12%~15%P and 5%~6%W was obtained by use of appropriate bath composition and plating conditions. The as-deposited composite coating is amorphous and it becomes mixture when the temperature is raised from 200℃to 400℃. However,
the composite coating is crystal when the temperature is over 400℃. Scanning electron microscopy indicates that the heat treatment temperature has no effect on the surface morphologies of the RE-Ni-W-P-SiC composite coating. This is to say that the composite coating has a better heat stability of microstructure and high temperature oxidation.
Key words: electrodeposition; RE-Ni-W-P-SiC composite coating; microstructure