中國有色金屬學報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 20 No. 5 May 2010 |
ZOU Gui-sheng(鄒貴生), CHEN Qiang(陳 強), REN Jia-lie(任家烈)
（Key Laboratory for Advanced Materials Processing Technology of the Ministry of Education,
Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China）
Abstract:The mechanical properties of Ti-23Al-17Nb (mole fraction, %) laser beam welding alloy joint at room temperature are comparable to that of the base materials. However, the strength and ductility of the as-welded joint deteriorate seriously after high temperature circulation. The effect of post-welded heat treatment on the microstructure and mechanical properties of the joint was investigated. The heat treatment was taken at 980 ℃ for 1.5 h, then furnace cooling and air cooling were performed separately. The results indicate that proper post-welded heat treatment improves the ductility of the joint at high temperature.
Key words: Ti-23Al-17Nb; Ti3Al-based alloy; laser beam welding; post-weld heat treatment; mechanical properties