中國有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 19 No. 5 October 2009 |
LI Xin(李 欣)1, 2, SONG Hua-xiao(宋華曉)1, 2, PENG Qing-qing
（1. College of Environmental Science and Engineering, Hunan University, Changsha 410082, China;
2. Key Laboratory of Environmental Biology and Pollution Control of Ministry of Education,
Hunan University, Changsha 410082, China）
Abstract:The experiments were conducted to evaluate the Cr(Ⅵ) resistance and reduction by Pseudomonas aeruginosa. After this bacterium tolerated 40 mg/L Cr(Ⅵ), the growth of cells was observed. The bacterial growth was obviously lower than the controls over 24 h and the binary cell fission was observed in cell morphology by scanning electron microscope. P. aeruginosa was found to be able to reduce Cr(Ⅵ) although Cr(Ⅵ) had toxic effects on the cells. The results demonstrate that Cr(Ⅵ) is reduced from 40 mg/L to about 18 mg /L in 72 h. The value of pH drops from 7.02 to around 5.65 after 72 h. A significant increase in the value of redox potential occurs during Cr(Ⅵ) reduction and Cr(Ⅵ) reduction can be observed over a range of redox potential from +3 mV to +91 mV. Both of SO42− and NO3− have no effect on Cr(Ⅵ) reduction. The presence of Zn2+ has a notable inhibitory effect on Cr(Ⅵ) reduction while Cu2+ substantially stimulates Cr(Ⅵ) reduction. In the presence of Zn2+, Cr(Ⅵ) decreases from 40 mg/L to only 26−27 mg/L, whereas Cr(Ⅵ) drops to 1−2 mg/L after 48 h in the presence of Cu2+.
Key words: Pseudomonas aeruginosa; Cr(Ⅵ) reduction; Cr(Ⅵ) resistance; bacterial growth