中國有色金屬學報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 13 No. 6 December 2003 |
nitrogen then titanium
SUN Yue(孫 躍)1, LIU Wei-min(劉維民)2,
XU Tao(徐 洮)
（1.School of Materials Science and Engineering,
Harbin Institute of Technology, Harbin 150001, China;
2.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, the Chinese Academy of Sciences, Lanzhou 730000, China）
Abstract:2024 aluminum alloy was implanted with nitrogen then titanium at different titanium target sputtering currents by plasma-based ion implantation(PBII). The appearances were observed by atomic force microscope, and the surface hardness was measured with Knoop hardness tester and the mechanical property microprobe. Ball-on-disc dry wear experiments were performed under ambient air conditions, to study the tribological properties of the modified layers against GCr15 steel ball, employing various loads and a constant sliding speed. After dual modifications, surface hardness at 100nm depth could reach to 9GPa, increasing by about 5 times; tribological properties at lower load(e.g. 1N) were obviously improved, with the friction coefficient(below 0.2) decreasing by over 60%, and the wear life(800 times) increasing by about 5 times. Meanwhile, with the increase of the sputtering current, the appearance is smooth, the surface hardness tends to a slow and even variation, the wear life presents a parabola-like change, and the friction coefficient and the adhesive wear degree decrease. However, tribological properties are reduced with the increase of the load due to the modified layer rapidly getting thin.
Key words: aluminum alloy; plasma-based ion implantation; sputtering current; tribological properties