BI Jian-qiang(畢見強(qiáng)), YIN Yan-sheng(尹衍升),
ZHANG Yu-jun(張玉軍)
（Key Laboratory for Liquid Structure and Heredity of Materials, Ministry of Education China, Shandong University, Ji＇nan 250061, China）
Abstract:When Cr, Mo and Ti were added to Fe-Al/Al2O3 composite, the bending strength and fracture toughness of the composite were increased sharply. The highest value of bending strength can exceed 600MPa and the average value of fracture toughness exceed 12MPa·m1/2. With increasing content of Mo and Ti, the bending strength and fracture toughness both express the trend of increasing first and then decreasing. When the alloying elements were added to the composites the alloying extent is improved. The fracture mode of the composites are mainly transcrystalline.
Key words: Fe-Al intermetallic; Al2O3; composite; alloying element