中國有色金屬學(xué)報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 15 No. 2 April 2005 |
XIONG Yu-hua(熊玉華)3, ZHANG Rong(張 蓉)1
（1. State Key Laboratory of Solidification Processing,
Northwestern Polytechnical University, Xi'an 710072, China;
2. Department of Mechanical Engineering, Xi'an Petroleum Institute,
Xi'an 710065, China;
3. Beijing General Research Institute for Non-ferrous Metals, Beijing 100088, China）
Abstract:Grain refinement of superalloy K4169 was achieved by adding refiners into the alloy melt and their effects on the mechanical properties were investigated. The tensile properties at room temperature and 700℃ and low cycle fatigue properties at room temperature were compared for both conventional and fine grained test bars. The results indicate that the rupture strength, yield strength, elongation and reduction of area for refined grains are all much superior to those for coarse ones. Whereas the elongation and reduction of area of fine grained samples decrease at 700℃. Low cycle fatigue properties of samples with refined grains at room temperature are improved significantly. In addition, the degree of dispersion of low cycle fatigue data of samples with refined grains is diminished.
Key words: superalloy; grain refinement; refiner; tensile properties; LCF