中國有色金屬學報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 14 No. 1 February 2004 |
powder①
（1. School of Chemistry and Chemical Engineer, Central South University, Changsha 410083, China;
2. School of Chemistry and Chemical Engineer, Anhui University, Hefei 230039, China）
Abstract:Hard zinc from thermo-plating zinc factory had been treated for preparation of ZnO nano-powder by chemical precipitation. The ion-type and non-ion-type surface-active reagents were added in different steps and ultrasonic agitation was used in preparing process. TG/DTG was applied to determine thermo-decomposition temperature of the precursor as about 450℃. The product is light yellow, and had been characterized by XRD,SBETand TEM, through which the good dispersing sphere particles with the average diameter of approximately 50 60 nm are observed, and the crystal is pure ZnO with hexahedral structure. The cost of preparing nanometer zinc oxide is low.
Key words: zinc oxide; nanoparticle; ultrasonic wave; surface-active reagent