中國有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 18 No. 3 June 2008 |
（1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;2. School of Materials Science and Engineering, Harbin University of Science and Technology, Harbin 150040, China;3. Beijing Institute of Aeronautical Materials, Beijing 100095, China）
Abstract:The hot compression testing of hot isostatically pressed(HIPed) spray formed(SF) nickel-base superalloy was carried out by thermal mechanical simulator in the temperature range of 1 050−1 140 ℃ at strain rates of 0.01−10 s−1 and engineering strain of 50%. A processing map was developed on the basis of these data by using the principles of dynamic materials modeling. The microstructural evolution of deformed samples was also examined on the basis of optical and electron microscopic observations. The map exhibits two domains: the instability domain at the temperatures of 1 050 ℃−1 110 ℃ and strain rate of 0.01 s−1, the stability domain at the temperatures of 1 110 ℃−1 140 ℃ and strain rates of 1 s−1−10 s−1, with a peak efficiency of about 40%. The dynamic recrystallization(DRX) is observed in the stability domain and the deformed specimens are no cracking or instabilities. However, there is no DRX in the instability domain and the alloy exhibits flow instability with cracks due to poor workability. The optimum hot working condition was determined in the stability domain.
Key words: spray forming; nickel-base superalloy; hot compression; processing map; recrystallization