中國有色金屬學(xué)報(bào)(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 17 No. 2 April 2007 |
and hot workability of high strength
7B04 aluminium alloy
（1. School of Materials Science and Engineering, Central South University,
Changsha 410083, China;
2. Northeast Light Alloy Co. Ltd, Harbin 150060, China）
Abstract:The effects of homogenization treatment on microstructure, overburnt temperature and hot rolling plasticity of high strength 7B04 aluminium alloy were investigated. Under the condition of homogenization at 470 ℃, the starting melting temperature of the primary eutectics in ingot of non-equilibium solidified 7B04 alloy is 478 ℃. Using two-step homogenization processing at ultra-high temperature which comprises heating the ingots to 470 ℃ at 10 ℃/h and holding for 64 h, and then heating to 500 ℃ at 1 ℃/h and holding for 10 h, the ingots of 7B04 aluminium alloy could safely pass the sensitive overburnt zone between 480 ℃ and 495 ℃, and the ordinary burnt phenomena of the ingots between 480 ℃ and 495 ℃ does not occur because the excess low-melting point eutectic phases in the as-cast alloy dissolve into the matrix during the two-step homogenization processing. Consequently, the hot rolling plasticity of ingot of 7B04 aluminium alloy is greatly improved.
Key words: 7B04 aluminium alloy; homogenization; low-melting point eutectic phases; overburnt temperature