中國有色金屬學報(英文版)
Transactions of Nonferrous Metals Society of China
| Vol. 17 No. 1 January 2007 |
oxidized for vanadium redox battery
application
TAN Ning(譚 寧)1, CHEN Li-quan(陳立泉)1, 2
（1. School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China;
2. Institute of Physics, Chinese Academy of Sciences, Beijing 100080, China）
Abstract: The graphite felt was oxidized at a positive electrode potential in sulfuric acid solution. The electrochemical performance of the treated graphite felt served as electrode for vanadium redox battery was investigated with FT-IR, SEM, XPS, BET, cyclic voltammetry and testing VRB system, respectively. The results show that the molar ratio of O to C increases from 0.085 to 0.15 due to the increase of —COOH functional groups during electrochemical oxidation treatment, and the GF surface is eroded by electrochemical oxidation, resulting in the surface area increase from 0.33 m2/g to 0.49 m2/g. The VRB with modified GF electrode exhibits excellent performance under a current density of 30 mA/cm2. The average current efficiency reaches 94% and average voltage efficiency reaches 85%. The improvement of electrochemical activity for the electrode is ascribed to the increase of the number of —COOH group and the special surface of GF.
Key words: vanadium redox battery; graphite felt; electrochemical oxidation